http://hdl.handle.net/11452/32651| Başlık: | Influence of oxide layer coating on giant magneto-impedance response in amorphous ribbons |
| Yazarlar: | Meydan, Turgut Uludağ Üniversitesi/Fen-Edebiyat Fakültesi/Fizik Anabilim Dalı. Taysioğlu, Asli Ayten Peksoz, Ahmet Derebaşı, Naim AAI-2254-2021 AAG-9772-2021 18038658800 23100976500 11540936300 |
| Anahtar kelimeler: | Chemistry Electrochemistry Instruments & instrumentation Physics Amorphous magnetic materials Giant magneto impedance effect Coating effect Atomic force microscopy Thin-films Zns Gmi Amorphous silicon Atomic force microscopy Coatings Magnetic materials Amorphous magnetic materials Amorphous ribbon Coating process Giant magneto impedance effect Giant magneto-impedance Oxide layer coatings Room temperature Successive ionic layer adsorption and reactions Molybdenum oxide |
| Yayın Tarihi: | Oca-2013 |
| Yayıncı: | Amer Scientific Publishers |
| Atıf: | Taysioglu, A. A. vd. (2013). “Influence of oxide layer coating on giant magneto-impedance response in amorphous ribbons”. Sensor Letters, 11(1), Special Issue, 119-121. |
| Özet: | Cobalt-rich amorphous ribbon (Fe5.85Co72.15Mo2B15Si5) 13 mm in length and 5 mm in width were coated with different oxide layers in order to improve their GMI response. The coating process was performed using a chemical Successive Ionic Layer Adsorption and Reaction (SILAR) technique at room temperature. Oxide layer coated ribbons were imaged by an Atomic Force Microscopy (AFM). The variations in oxide layers and their roughness were studied to elucidate the cause of the improvements in GMI ratios in amorphous ribbons. |
| URI: | https://doi.org/10.1166/sl.2013.2817 http://hdl.handle.net/11452/32651 |
| ISSN: | 1546-198X |
| Koleksiyonlarda Görünür: | Scopus Web of Science |
Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.
DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.