Başlık: The effect of post-weld heat treatment on the mechanical properties of 2024-T4 friction stir-welded joints
Yazarlar: Durgun, İsmail
Uludağ Üniversitesi/Mühendislik Fakültesi/Makine Mühendisliği Bölümü.
0000-0003-4280-3381
Aydın, Hakan
Bayram, Ali
AAH-6014-2019
16312009400
7004197848
36949060800
Anahtar kelimeler: Heat treatments
Welding
Mechanical
Abnormal grain-growth
Aluminum-alloy joints
Tensile properties
Fracture-behavior
Microstructure
Materials science
Friction
Heat treatment
Mechanical properties
Welded steel structures
Welds
2024 aluminum alloy
Ageing treatments
Base material
C. Heat treatments
E. Mechanical
Friction stir
Post weld heat treatment
Solution heat treatment
Weld zone
Welded joints
Welding
Yayın Tarihi: May-2010
Yayıncı: Elsevier
Atıf: Aydın, H. vd. (2010). "The effect of post-weld heat treatment on the mechanical properties of 2024-T4 friction stir-welded joints". Materials & Design, 31(5), 2568-2577.
Özet: In this study, the effect of post-weld heat treatment (PWHT) on the mechanical properties of friction stir-welded 2024 aluminum alloys in the T4 temper state was investigated. Solution heat treatment and various ageing treatments were given to the welded joints. The PWHT procedures caused abnormal coarsening of the grains in the weld zone, which resulted in a drop in micro-hardness at the weld zone compared to the base material of the joints. T6 (190 degrees C - 10 h) ageing treatment after welding was found to be more beneficial than the other heat treatments in enhancing the mechanical properties of the 2024-T4 joints. However, the T6 (190 degrees C - 10 h) heat treatment led to significant ductility deterioration in the joint.
URI: https://doi.org/10.1016/j.matdes.2009.11.030
https://www.sciencedirect.com/science/article/pii/S0261306909006499
http://hdl.handle.net/11452/22416
ISSN: 0261-3069
Koleksiyonlarda Görünür:Scopus
Web of Science

Bu öğenin dosyaları:
Bu öğeyle ilişkili dosya bulunmamaktadır.
Tüm Öğe Kaydını Göster İstatistikler


DSpace'deki bütün öğeler, aksi belirtilmedikçe, tüm hakları saklı tutulmak şartıyla telif hakkı ile korunmaktadır.