dc.identifier.citationAkay, S. K. vd. (2009). "Fatigue life behaviour of the dual-phase low carbon steel sheets". Journal of Materials Processing Technology, 209(7), 3358-3365.en_US
dc.identifier.issn0924-0136-
dc.identifier.urihttps://doi.org/10.1016/j.jmatprotec.2008.07.038-
dc.identifier.urihttps://www.sciencedirect.com/science/article/pii/S0924013608006055-
dc.identifier.urihttp://hdl.handle.net/11452/23004-
dc.description.abstractThis paper presents the effect of heat treatment on the fatigue life of low carbon steel sheet with dual-phase microstructure. The steel sheets were heat treated with two different procedures; intermediate quenching, intermediate quenching and tempering. The properties of tensile strength, fatigue life, hardness, micro hardness and microstructure were evaluated by the mechanical tests and metallographic analysis, respectively. The results showed that dual-phase steel (DPS) microstructures, composed by ferrite and martensite had higher fully reversed plane bending fatigue strength when compared with as-received steel and tempered martensite (TM) steel. The experimental results showed that fatigue life of the heat-treated steel sheets enhanced with increasing amount of martensite in the microstructure. The highest fatigue strength was observed on the intermediately annealed steel sheets at 870 degrees C. Internal microstructures, fatigue crack initiation and propagation of the heat-treated steel were analyzed by scanning electron microscopy (SEM).en_US
dc.description.sponsorshipTürkiye Cumhuriyeti Kalkınma Bakanlığı - DPT (F-2005/4)tr_TR
dc.language.isoenen_US
dc.publisherElsevier Scienceen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectDual phase steelen_US
dc.subjectFatigue lifeen_US
dc.subjectIntermediate heat treatmenten_US
dc.subjectMicrostructureen_US
dc.subjectMechanical-propertiesen_US
dc.subjectHeat-treatmenten_US
dc.subjectMartensiteen_US
dc.subjectTensileen_US
dc.subjectMicrostructureen_US
dc.subjectMorphologyen_US
dc.subjectEngineeringen_US
dc.subjectMaterials scienceen_US
dc.subjectBending strengthen_US
dc.subjectCarbon steelen_US
dc.subjectCracksen_US
dc.subjectFatigue of materialsen_US
dc.subjectHardnessen_US
dc.subjectHeat treating furnacesen_US
dc.subjectMartensiteen_US
dc.subjectMetallographyen_US
dc.subjectMicrostructureen_US
dc.subjectPaper sheetingen_US
dc.subjectQuenchingen_US
dc.subjectScanning electron microscopyen_US
dc.subjectSuperconducting wireen_US
dc.subjectZinc platingen_US
dc.subjectBending fatiguesen_US
dc.subjectDual phase steelen_US
dc.subjectDual-phase microstructuresen_US
dc.subjectFatigue crack initiationsen_US
dc.subjectFatigue lifeen_US
dc.subjectFatigue strengthsen_US
dc.subjectFully reverseden_US
dc.subjectIntermediate heat treatmenten_US
dc.subjectInternal microstructuresen_US
dc.subjectLow carbon steel sheetsen_US
dc.subjectMechanical testsen_US
dc.subjectMetallographic analysisen_US
dc.subjectMicro hardnessen_US
dc.subjectQuenching and temperingen_US
dc.subjectSemen_US
dc.subjectTempered martensitesen_US
dc.subjectSteel sheeten_US
dc.titleFatigue life behaviour of the dual-phase low carbon steel sheetsen_US
dc.typeArticleen_US
dc.identifier.wos000265315000030tr_TR
dc.identifier.scopus2-s2.0-62949208705tr_TR
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergitr_TR
dc.contributor.departmentUludağ Üniversitesi/Fen-Edebiyat Fakültesi/Fizik Bölümü.tr_TR
dc.contributor.departmentUludağ Üniversitesi/Teknik Bilimler Meslek Yüksekokulu.tr_TR
dc.contributor.departmentUludağ Üniversitesi/Mühendislik Fakültesi/Makina Mühendisliği Bölümü.tr_TR
dc.relation.bap2004/54tr_TR
dc.contributor.orcid0000-0002-8720-7594tr_TR
dc.identifier.startpage3358tr_TR
dc.identifier.endpage3365tr_TR
dc.identifier.volume209tr_TR
dc.identifier.issue7tr_TR
dc.relation.journalJournal of Materials Processing Technologyen_US
dc.contributor.buuauthorAkay, Sertan Kemal-
dc.contributor.buuauthorYazıcı, Murat-
dc.contributor.buuauthorBayram, Ali-
dc.contributor.buuauthorAvinç, Ahmet-
dc.contributor.researcheridR-7260-2016tr_TR
dc.contributor.researcheridM-4741-2017tr_TR
dc.subject.wosEngineering, industrialen_US
dc.subject.wosEngineering, manufacturingen_US
dc.subject.wosMaterials science, multidisciplinaryen_US
dc.indexed.wosSCIEen_US
dc.indexed.scopusScopusen_US
dc.wos.quartileQ2en_US
dc.wos.quartileQ1 (Engineering, manufacturing)en_US
dc.contributor.scopusid24801954600tr_TR
dc.contributor.scopusid7007162323tr_TR
dc.contributor.scopusid7004197848tr_TR
dc.contributor.scopusid6506411792tr_TR
dc.subject.scopusDual Phase Steel; Martensite; Dp600en_US
Appears in Collections:Scopus
Web of Science

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.